High Quality Injection PVDF Powder for Coating Raw Material

• Feature: Chemical Resistance
• CAS No.: 24937-79-9
• Formula: C2h2f2
• EINECS: 24937-79-9
• Material: Fluoropolymer PVDF
• Usage: Specialty Plastics
• Model NO.: FL2611
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection Grade
• Color: White
• Features: Copolymer, Low Melt Viscosity
• Forms: White Powder or White Translucent Particles
• Mfr: 20.0~30.0
• Applications: Injection/Powder Coating
• Transport Package: 25kg/Bag
• Specification: White Powder
• Trademark: Zheflon
• Origin: China
• HS Code: 3904690090
• Production Capacity: 25000tons/Year

Product Description

Product Description

Zheflon^® FL2611 PVDF- Injection Grade

Zheflon® FL2611 is a polyvinylidene fluoride copolymer with a low melt viscosity grade and is particularly suitable for applications in coatings and cable industries. It has the typical characteristics of thermoplastic fluororesin. It has excellent chemical stability, temperature resistance, corrosion resistance, weather resistance to most active substances and solvents. It gives the cable excellent mechanical properties, flexibility and electrical properties, high temperature resistance and corrosion resistance, low flammability and smoky.
 

 

Data Sheet

 

General
Features	Copolymer, low melt viscosity
Uses	Injection, powder coating
Forms	White powder or white translucent particles
Items	Typical Value	Test Method
Physical Properties
Density(g/cc)	1.77~1.80	ASTM D792
Melt Flow Rate(g/10min)	20.0~30.0	Load 5kg,230ºC,ASTM D1238
Water Absorption(%)(Time 24 hr)	≤0.10	ISO 62
Linear Mold Shrinkage(cm/cm)	0.0200~0.0300
Molecular Properties
Molecular weight(W Da)	18~22	GPC,DMF,ISO 16014
Intrinsic viscosity(dl/g)	0.8~0.9	30ºC,DMAC
Molecular weight distribution	2.0-3.0	GPC,DMF,ISO 16014
Mechanical Properties
Tensile Modulus(Thickness2.00mm)(MPa)	800~1000	1.0mm/min,ASTM D638
Yield Strength(Thickness2.00mm)(MPa)	20~35	50mm/min,ASTM D638
Break Strength(Thickness2.00mm)(MPa)	20~30	50mm/min,ASTM D638
Elongation at Yield(%)	10~20	50mm/min,ASTM D638
Elongation at Break(%)	≥300	50mm/min,ASTM D638
Hardness, Shore D(Thickness2.00mm)	65~75	ASTM D2240
Thermal Properties
Melting Point(ºC)	130~140	ASTM D3418
Decomposition Temperature(ºC)	≥350	1% wt. loss / in air

Packing & Storage

• Process safety instructions

1. This product should be processed under 260ºC to avoid producing toxic gases.
2. PVDF has good fire resistance and smoke inhibition property. While, it will release toxic gas and fluorocarbon. compounds when meets with fire.
3. Operators should pay attention to personal protection during the processing and operating.

• Packaging and storage

PVDF is packed in a plastic bag and then be put into a PE bag with the net weight 25KGS. It must be stored in clean, cool, dry place.

 

Product Applications

 

Company Profile

 

FLURINE is a technological enterprise established in 2007 that integrates R&D, production and sales of PVDF and FKM raw materials.

We have a first-class core technology research and development team. After more than ten years of painstaking research, it has continuously expanded its product application fields, covering lithium batteries, films, cables, chemical materials and other industries.

We owns a multi-channel, multi-level R&D team of new materials, adhere to the combination of research and development and the introduction of advanced technology at home and abroad. We upgrade our products through technological innovation and change the existing product mix to meet the widest range of market needs.

Adhering to the people-oriented business philosophy, we also pay attention to the harmonious coexistence between man and nature, and are committed to creating a win-win world between man and nature. At present, We have established cooperative relations with major domestic lithium battery enterprises, and has become the world's largest PVDF production base.
 

Certificates