High Performance Copolymer PVDF for Wires and Cables Best Price

• Feature: Chemical Resistance
• CAS No.: 24937-79-9
• Formula: C2h2f2
• EINECS: 24937-79-9
• Material: Fluoropolymer PVDF
• Usage: Specialty Plastics
• Model NO.: FL2608
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection Grade
• Color: White
• Features: Copolymer, Low Viscosity
• Forms: Translucent White Particles
• Mfr: 15.0~25.0
• Applications: Wire/Cable
• Transport Package: 25kg/Bag
• Specification: White Particles
• Trademark: Zheflon
• Origin: China
• HS Code: 3904690090
• Production Capacity: 25000tons/Year

Product Description

Product Description

Zheflon^® FL2608 PVDF- Injection Grade

Zheflon^®FL2608 PVDF copolymer is low viscosity grade, especially suitable for applications in the cable industry. It gives the cable excellent mechanical properties, flexibility and electrical performance; high temperature corrosion resistance; low flammability, smoke emission. In addition, the zero-perfluorooctanoic acid and heavy metal content to comply with RoHS requirements.
 

 

Data Sheet

 

General
Features	Copolymer, Low viscosity
Uses	Wire, Cable
Forms	Translucent white particles
Items	Typical Value FL2608	Test Method
Physical Properties
Density(g/cc)	1.77~1.80	ASTM D792
Melt Flow Rate(g/10min)	15.0~25.0	Load 5kg,230ºC,ASTM D1238
Melt viscosity(Kps)	6~9	Shear Rate 100 1/s,ASTM D3835
Water Absorption(%)(Time 24 hr)	≤0.040	ISO 62
Linear Mold Shrinkage(cm/cm)	0.0200~0.0300
Molecular Properties
Molecular weight(Da)	250,000~280,000	GPC,DMF,ISO 16014
Intrinsic viscosity(dl/g)	0.85~1.00	30ºC,DMAC
Molecular weight distribution	2.0-3.0	GPC,DMF,ISO 16014
Mechanical Properties
Tensile Modulus(Thickness2.00mm)(MPa)	600~1000	1.0mm/min,ASTM D638
Flexural Modulus(Thickness2.00mm)(MPa)	800~1000	2.0mm/min,ASTM D790
Yield Strength(Thickness2.00mm)(MPa)	25.0~35.0	50mm/min,ASTM D638
Break Strength(Thickness2.00mm)(MPa)	20.0~30.0	50mm/min,ASTM D638
Elongation at Yield(%)	10.0~15.0	50mm/min,ASTM D638
Elongation at Break(%)	200~600	50mm/min,ASTM D638
Hardness, Shore D(Thickness2.00mm)	70~75	ASTM D2240
Izod Impact, Notched(Thickness 4.00mm, 23ºC)(J/m)	100~150	Notched V 10 mm ASTM D256
Thermal Properties
Melting Point(ºC)	158~166	ASTM D3418
Crystallization Temperature(DSC peak)(ºC)	115~130	ASTM D3418
Glass Transition Temp, Tg(ºC)	-32.0	ASTM E1356
Decomposition Temperature(ºC)	330~350	1% wt. loss / in air
Vicat Softening Point(ºC)	90~105	ASTM D1525
Heat deflection temperature at 1.8 MPa(Thickness 4.00mm)(ºC)	50~60	After annealing 150ºC,16h ASTM D648
Electrical Properties
Surface Resistance(ohm)	≥1.00E+14	Voltage<1V,After 2 min-500V ASTM D257
Electrical Resistivity(ohm·cm)	≥1.00E+14	Intensity=10mA,After 2 min@23ºC ASTM D257
Dielectric strength(Thickness 1.00mm,23ºC)(KV/mm)	20~25	ASTM D149
Dielectric constant(1kHz,23ºC)	7.0~10.0	ASTM D150
Burning Properties
UL Flame retardant grade(0.100mm)	V-0	UL94
Oxygen Index(3.00mm)	44%	ASTM D2683

Packing & Storage

• Process safety instructions

1. This product should be processed under 260ºC to avoid producing toxic gases.
2. PVDF has good fire resistance and smoke inhibition property. While, it will release toxic gas and fluorocarbon. compounds when meets with fire.
3. Operators should pay attention to personal protection during the processing and operating.

• Packaging and storage

PVDF is packed in a plastic bag and then be put into a PE bag with the net weight 25KGS. It must be stored in clean, cool, dry place.

 

Product Applications

 

Company Profile

 

FLURINE is a technological enterprise established in 2007 that integrates R&D, production and sales of PVDF and FKM raw materials.

We have a first-class core technology research and development team. After more than ten years of painstaking research, it has continuously expanded its product application fields, covering lithium batteries, films, cables, chemical materials and other industries.

We owns a multi-channel, multi-level R&D team of new materials, adhere to the combination of research and development and the introduction of advanced technology at home and abroad. We upgrade our products through technological innovation and change the existing product mix to meet the widest range of market needs.

Adhering to the people-oriented business philosophy, we also pay attention to the harmonious coexistence between man and nature, and are committed to creating a win-win world between man and nature. At present, We have established cooperative relations with major domestic lithium battery enterprises, and has become the world's largest PVDF production base.
 

Certificates